Suchergebnisse

Funding Information: The authors gratefully acknowledge the European Commission for funding the InnoRenew project (Grant Agreement #739574 under the Horizon 2020 Widespread-2-Teaming program), the Republic of Slovenia (investment funding from the Republic of Slovenia and the European Regional Development Fund) and infrastructural ARRS program IO-0035. Part of this work was conducted during project BIO4ever (RBSI14Y7Y4), funded within call SIR by MIUR-Italy; the project Multi-spec (BI-IT/18-20-007), funded by ARRS-Slovenia; Archi-BIO (BI/US-20-054) funded by ARRS-Slovenia, J7-9404 (C) funded by ARRS-Slovenia, and CLICK DESIGN, ?Delivering fingertip knowledge to enable service life performance specification of wood?, (No. 773324) supported under the umbrella of ERA-NET Cofund ForestValue by the Ministry of Education, Science and Sport of the Republic of Slovenia. ForestValue has received funding from the European Union?s Horizon 2020 research and innovation programme. Funding Information: Funding: The authors gratefully acknowledge the European Commission for funding the InnoRenew project (Grant Agreement #739574 under the Horizon2020 Widespread-2-Teaming program), the Republic of Slovenia (investment funding from the Republic of Slovenia and the European Regional Development Fund) and infrastructural ARRS program IO-0035. Part of this work was conducted during project BIO4ever (RBSI14Y7Y4), funded within call SIR by MIUR-Italy; the project Multi-spec (BI-IT/18-20-007), funded by ARRS-Slovenia; Archi-BIO (BI/US-20-054) funded by ARRS-Slovenia, J7-9404 (C) funded by ARRS-Slovenia, and CLICK DESIGN, "Delivering fingertip knowledge to enable service life performance specification of wood", (No. 773324) supported under the umbrella of ERA-NET Cofund ForestValue by the Ministry of Education, Science and Sport of the Republic of Slovenia. ForestValue has received funding from the European Union's Horizon 2020 research and innovation programme. Publisher Copyright: © 2021 by the authors. Licensee MDPI, Basel, Switzerland. ; The service life performance of timber products exposed to natural weathering is a critical factor limiting the broad use of wood as an external building element. The goal of this study was to investigate the in-service characterization of an innovative biofinish coating system. It is a novel surface finishing solution based on the bioinspired concept of living fungal cells designed for effective wood protection. The performance of Scots pine (Pinus sylvestris L.) wood coated with biofinish was compared with uncoated references. Samples were exposed to natural weathering for 12 months under the climatic conditions of northern Italy. The visual appearance, colour, gloss, wettability, and 3D surface topography of the wood surface were examined. Results revealed that the total colour changes (∆E) of biofinish-coated wood were negligible. Untreated Scots pine wood revealed the changes in colour after just three months of exposure. The gloss changes of both surface types were small. The contact angle measured on biofinish-coated wood was higher compared to that of uncoated Scots pine. Surface roughness increased in uncoated wood due to the erosion effect caused by the weathering progress. Conversely, the surface roughness of biofinish-coated samples decreased along the exposure time. This phenomenon was explained by two self-healing mechanisms: migration of non-polymerized oil to the cracked surface, where it polymerizes and creates a closed layer, and local regrowth to cover damaged spots by living fungal cells present in the coating. The obtained results revealed the superior aesthetic performance of the biofinish surface treatment against natural weathering. By considering the fully bio-based nature of the investigated coating, it was concluded that this solution can be an attractive alternative for state-of-the-art wood protection technologies. ; Peer reviewed