In Situ Observations of the Deformation Behavior and Fracture Mechanisms of Ti-45Al-2Nb-2Mn+0.8 vol pct TiB₂
Abstract
The deformation and fracture mechanisms of a nearly lamellar Ti-45Al-2Nb-2Mn (at. pct) + 0.8 vol pct TiB₂ intermetallic, processed into an actual low-pressure turbine blade, were examined by means of in situ tensile and tensile-creep experiments performed inside a scanning electron microscope (SEM). Low elongation-to-failure and brittle fracture were observed at room temperature, while the larger elongations-to-failure at high temperature facilitated the observation of the onset and propagation of damage. It was found that the dominant damage mechanisms at high temperature depended on the applied stress level. Interlamellar cracking was observed only above 390 MPa, which suggests that there is a threshold below which this mechanism is inhibited. Failure during creep tests at 250 MPa was controlled by intercolony cracking. The in situ observations demonstrated that the colony boundaries are damage nucleation and propagation sites during tensile creep, and they seem to be the weakest link in the microstructure for the tertiary creep stage. Therefore, it is proposed that interlamellar areas are critical zones for fracture at higher stresses, whereas lower stress, high-temperature creep conditions lead to intercolony cracking and fracture. ; The authors are grateful to Industria de Turbo Propulsores, S.A. for supplying the intermetallic blades. Funding from the Spanish Ministry of Science and Innovation through projects MAT2009-14547-C02-01 and MAT2009-14547-C02-02 is acknowledged. The Madrid Regional Government supported this project partially through the ESTRUMAT grant P2009/MAT-1585. C.J.B. acknowledges the support from Grant SAB2009-0045 from the Spanish Ministry of Education for his sabbatical stage in Madrid. ; Publicado
Problem melden