Eutectic modification by ternary compound cluster formation in Al-Si alloys

Open Access

Abstract

Al-alloys with Si as the main alloying element constitute the vast majority of Al castings used commercially today. The eutectic Si microstructure in these alloys can be modified from plate-like to coral-like by the addition of a small amount of a third element to improve ductility and toughness. In this investigation the effects of Eu and Yb are studied and their influence on the microstructure is compared to further understand this modification. The two elements impact the alloy differently, where Eu modifies Si into a coral-like structure while Yb does not. Atom probe tomography shows that Eu is present within the Si phase in the form of ternary compound Al2Si2Eu clusters, while Yb is absent in the Si phase. This indicates that the presence of ternary compound clusters within Si is a necessary condition for the formation of a coral-like structure. A crystallographic orientation relationship between Si and the Al2Si2Eu phase was found, where the following plane normals are parallel: 011(Si) //0001(Al2Si2Eu), 111(Si)//6 (7) over bar 10(Al2Si2Eu) and 011(Si)//6 (7) over bar 10(Al2Si2Eu). No crystallographic relationship was found between Si and Al2Si2Yb. The heterogeneous formation of coherent Al2Si2Eu clusters inside the Si-phase is suggested to trigger the modification of the microstructure. ; Funding Agencies|European Regional Development Fund (ERDF); DFG; Federal State Government of Saarland [INST 256/298-1 FUGG]; Erasmus Mundus Programme of the European Commission within the Doctoral Programme DocMASE; Major International (Regional) Joint Research Project from China [51420105005]; Overseas, Hong Kong, Macao Scholars Cooperative Research Fund from China [51728101]